5mm Oxidated Fecral Alloy Wire 0cr27al7mo2 For Industrial Furnace Heating

Shanghai Tankii Alloy Material Co.,Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now

5mm Oxidated Fecral Alloy Wire 0cr27al7mo2 For Industrial Furnace Heating

Brand Name : TANKII

Model Number : 0Cr27Al7Mo2

Certification : ISO9001:2008

Place of Origin : Shanghai

MOQ : 10 KG

Price : To negotiate

Payment Terms : L/C, T/T, Western Union, Paypal

Supply Ability : 200+TON+MONTH

Delivery Time : 7-12 days

Packaging Details : Spool, Carton, plywood case with plastic film as your requirements

Model name : 0Cr27Al7Mo2, 0Cr21Al6Nb, 0Cr25Al5, 0Cr23Al5

Application : Industrial Furnace Heating Elements

Advantages : Good corrosion resistance, good ductility, good elongation

Colour : Silver Grey, Oxidated Colour

Surface : Smooth, Soft, Annealed

Condition : Sofe, Half hard, Hard

Contact Now

Tinned Copper Wire SWG/AWG Standard with Good Corrosion Resistance for Marine Cable

5 mm 0Cr27Al7Mo2 Fecral Alloy Wire Oxidated Colour for Industrial Furnace Heating

FeCrAl alloy has the characteristic of high resistivity,low temperature resistance coefficient,high operating temperature,good anti-oxidation and anti-corrosion under high temperature.

It is widely used in industrial furnace, household appliances, industry furnace, metallurgy, machinery, aircraft, automotive, military and other industries producing heating elements and resistance elements.

FeCrAl alloy series: OCr15Al5,1Cr13Al4, 0Cr21Al4, 0Cr21Al6, 0Cr23Al5, 0Cr25Al5, 0Cr21Al6Nb,0Cr27Al7Mo2, and etc.

The alloy's high resistivity and extremely low electro-motive force (EMF) versus copper are highly desired properties in precision resistance wire. It also possesses high tensile strength, high resistance to corrosion and is non-magnetic.

The temperature coefficient of resistance of this material is very closely controlled by the addition of aluminum, manganese and silicon combined with critical processing controls.

FeCrAl alloy is supplied in the annealed and heat treated condition to ± 5 ppm in the temperature range of -67°F to 221°F (-55°C to 105°C). This results in very stable resistance.

Although FeCrAl alloy is the only high-resistance, low-TCR alloy on which extensive stability tests have been conducted, EVANOHM alloy S is heat treated in the same manner and is believed to have equal stability because its properties are produced by the same short range ordering as FeCrAl alloy.

Size dimension range:

Wire: 0.01-10mm

Ribbon: 0.05*0.2-2.0*6.0mm

Strip: 0.05*5.0-5.0*250mm

Bar:10-50mm

Chemical Composition and Main Property of Fe-Cr-Al Resistance Alloy
Properties Grade 1Cr13Al4 0Cr25Al5 0Cr21Al6 0Cr23Al5 0Cr21Al4 0Cr21Al6Nb 0Cr27Al7Mo2
Main Chemical Composition
(%)
Cr 12.0-15.0 23.0-26.0 19.0-22.0 22.5-24.5 18.0-21.0 21.0-23.0 26.5-27.8
Al 4.0-6.0 4.5-6.5 5.0-7.0 4.2-5.0 3.0-4.2 5.0-7.0 6.0-7.0
Re opportune opportune opportune opportune opportune opportune opportune
Fe Bal. Bal. Bal. Bal. Bal. Bal. Bal.






Nb0.5 Mo1.8-2.2
Max Continuous Service Temperature(oC) 950 1250 1250 1250 1100 1350 1400
Resisivity 20oC (Ωmm2/m) 1.25
±0.08
1.42
±0.06
1.42
±0.07
1.35
±0.07
1.23
±0.07
1.45
±0.07
1.53
±0.07
Density(g/cm3) 7.4 7.1 7.16 7.25 7.35 7.1 7.1
Thermal Conductivity 52.7 46.1 63.2 60.2 46.9 46.1 45.2
(KJ/m@h@oC)
Coefficient of Thermal Expansion(α×10-6/oC) 15.4 16 14.7 15 13.5 16 16
Approximate Melting Point( oC) 1450 1500 1500 1500 1500 1510 1520
Tensile Strength(N/mm2) 580-680 630-780 630-780 630-780 600-700 650-800 680-830
Elongation(%) >16 >12 >12 >12 >12 >12 >10
Section Variation 65-75 60-75 65-75 65-75 65-75 65-75 65-75
Shrink Rate (%)
Repeatedly Bend Frequency(F/R) >5 >5 >5 >5 >5 >5 >5
Hardness (H.B.) 200-260 200-260 200-260 200-260 200-260 200-260 200-260
Continuous Service Time no ≥80/1300 ≥80/1300 ≥80/1300 ≥80/1250 ≥50/1350 ≥50/1350
Micrographic Structure Ferrite Ferrite Ferrite Ferrite Ferrite Ferrite Ferrite
Magnetic Property Magnetic Magnetic Magnetic Magnetic Magnetic Magnetic Magnetic

5mm Oxidated Fecral Alloy Wire 0cr27al7mo2 For Industrial Furnace Heating

5mm Oxidated Fecral Alloy Wire 0cr27al7mo2 For Industrial Furnace Heating5mm Oxidated Fecral Alloy Wire 0cr27al7mo2 For Industrial Furnace Heating

5mm Oxidated Fecral Alloy Wire 0cr27al7mo2 For Industrial Furnace Heating


Product Tags:

electrical heating wire

      

high temperature wire

      
Wholesale 5mm Oxidated Fecral Alloy Wire 0cr27al7mo2 For Industrial Furnace Heating from china suppliers

5mm Oxidated Fecral Alloy Wire 0cr27al7mo2 For Industrial Furnace Heating Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shanghai Tankii Alloy Material Co.,Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)